Structural composites are increasingly being utilized in many large naval and civil structures where it is vital that their long-term performance be predictable and their variability definable over the life of the structure. However, these properties may be influenced by the degree of cure of the resin, particularly for room-temperature-cured systems. Thus, this investigation defines the postcure effects on E-glass/vinyl-ester fiber-reinforced polymer (FRP) composites manufactured using the vacuum-assisted resin transfer molding (VARTM) method, which are typical of those used by the US Navy for ship structures. The composites are differentiated by varying levels of postcure temperature and duration, and examined for the effects of advancing cure at various points in the time after postcure. Pseudo-quasi-isotropic [0/+45/90/−45/0]s and angle ply laminate [±45]2s samples from each level of postcure are examined at 1, 10, 30, 100, and 300 days after postcure in order to track strength, stiffness, failure strain, creep, and fatigue performance as functions of time. In parallel, the matrix polymer is inspected using FTIR (Fourier transform infrared spectroscopy) to directly assess the degree of conversion. Dynamic mechanical analysis and shrinkage measurements are also undertaken to assess the Tg and the amount of shrinkage undergone during post-curing, as well as the advancing of the level of cure during the prescribed aging time. Results suggest that the degree of conversion is limited to 80% for the vinyl-ester oligomer and 90–95% for styrene following a postcure of 93°C. It is observed that after 300 days of ambient storage the nonpostcured samples approach the degree of conversion exhibited by those postcured at 93°C, as measured by FTIR. Resin dominated quasi-static properties are greatly affected by the degree of cure, whereas fiber dominated properties are not. Where the degree of cure is comparatively low, viscoelastic properties cause greater changes in creep response as well as influencing fatigue performance.

1.
Venditti
,
R. A.
, and
Gillham
,
J. K.
, 1997, “
Relationship Between the Glass Transition Temperature (Tg) and Fractional Conversion for Thermosetting Systems
,”
J. Appl. Polym. Sci.
0021-8995,
64
(
1
), pp.
3
14
.
2.
Venditti
,
R. A.
, and
Gillham
,
J. K.
, 1995, “
Anomalous Behavior of Thermosetting Systems After Cure Versus Chemical Conversion: A Normalized Conversion-Temperature-Property Diagram
,”
J. Appl. Polym. Sci.
0021-8995,
56
(
13
), pp.
1687
1705
.
3.
Wisanrakkit
,
G.
, and
Gillham
,
J. K.
, 1990, “
Glass Transition Temperature (Tg) as an Index of Chemical Conversion for a High-Tg Amine/Epoxy System’s Chemical and Diffusion-Controlled Reaction Kinetics
,”
J. Appl. Polym. Sci.
0021-8995,
41
(
11-12
), pp.
2885
2929
.
4.
Verghese
,
N.
,
Potts
,
D.
, and
Shafi
,
A.
, 2003, “
Evolution of Glass Transition Temperature as a Function of Cure in Epoxy Vinyl-ester Resins
,” Composites 2003 Convention and Trade Show, Composites Fabricators Association.
5.
Pascault
,
J. P.
, and
Williams
,
R. J. J.
, 1990, “
Glass Transition Temperature Versus Conversion Relationships for Thermosetting Polymers
,”
J. Polym. Sci., Part B: Polym. Phys.
0887-6266,
28
(
1
), pp.
85
95
.
6.
Dibenedetto
,
A. T.
, 1987, “
Prediction of the Glass Transition Temperature of Polymers: A Model Based on the Principle of Corresponding States
,”
J. Polym. Sci., Part B: Polym. Phys.
0887-6266,
25
(
9
), pp.
1949
1969
.
7.
Couchman
,
P. R.
, 1981, “
Effect of Degree of Polymerization on Glass Transition Temperatures
,”
Polym. Eng. Sci.
0032-3888,
21
(
7
), pp.
377
380
.
8.
Hale
,
A.
,
Macosko
,
C. W.
, and
Bair
,
H. E.
, 1991, “
Glass Transition Temperature as a Function of Conversion in Thermosetting Polymers
,”
Macromolecules
0024-9297,
24
(
9
), pp.
2610
2621
.
9.
Cook
,
W. D
,
Simon
,
G. P.
,
Burchill
,
P. J.
,
Lau
,
M.
, and
Fitch
,
T. J.
, 1997, “
Curing Kinetics and Thermal Properties of Vinyl Ester Resins
,”
J. Appl. Polym. Sci.
0021-8995,
64
(
4
), pp.
769
781
.
10.
Scott
,
T. F.
,
Cook
,
W. D.
, and
Forsythe
,
J. S.
, 2002, “
Kinetics and Network Structure of Thermally Cured Vinyl Ester Resins
,”
Eur. Polym. J.
0014-3057,
38
(
4
), pp.
705
716
.
11.
Li
,
H.
,
Rosario
,
A. C.
,
Davis
,
S. V.
,
Glass
,
T.
,
Holland
,
T. V.
,
Davis
,
R. M.
,
Lesko
,
J. J.
,
Riffle
,
J. S.
, and
Florio
,
J.
, 1997, “
Network Formation of Vinyl Ester-Styrene Composite Matrix Resins
,”
J. Adv. Mater.
1070-9789,
28
(
4
), pp.
55
62
.
12.
Li
,
H.
,
Burts
,
E.
,
Bears
,
K.
,
Ji
,
Q.
,
Lesko
,
J. J.
,
Dillard
,
D. A.
,
Riffle
,
J. S.
, and
Puckett
,
P. M.
, 2000, “
Network Structure and Properties of Dimethacrylate-Styrene Matrix Materials
,”
J. Compos. Mater.
0021-9983,
34
(
18
), pp.
1512
1528
.
13.
Ziaee
,
S.
, and
Palmese
,
G. R.
, 1999, “
Effects of Temperature on Cure Kinetics and Mechanical Properties of Vinyl-Ester Resins
,”
J. Polym. Sci., Part B: Polym. Phys.
0887-6266,
37
(
7
), pp.
725
744
.
14.
Puckett
,
P. M.
,
Bradley
,
S. W.
,
Bradley
,
W. L.
, and
Sue
,
H.-J.
, 1997, “
Viscoelastic Creep Characteristics of Neat and E-Glass Reinforced Thermoset Resins
,”
Composites for Real World International SAMPE Technical Conf.
,
29
, pp.
157
167
.
15.
ASTM
, 2001, “
Standard Test Method for Plastics: Dynamic Mechanical Properties: In Flexure (Dual Cantilever Beam)
,” ASTM D 5418, Nov.
16.
ASTM
, 2000, “
Standard Test Method for Tensile Properties of Polymer Matrix Composite Materials
,” ASTM D 3039, July.
17.
ASTM
, 1995, “
Standard Test Method for In-Plane Shear Response of Polymer Matrix Composite Materials by Tensile Test of a ±45° Laminate
,” ASTM D 3518, Jan.
18.
ASTM
, 1996, “
Standard Test Method for Tension-Tension Fatigue of Polymer Matrix Composite Materials
,” ASTM D 3479, Aug.
You do not currently have access to this content.