The low-velocity impact response of a hybrid titanium composite laminate, known as , was compared to that of graphite/epoxy composite. The material comprised of two outer plies of titanium foil surrounding a composite core. The composite core was PIXA-M (a high temperature thermoplastic) reinforced by IM-6 graphite fibers and consolidated by an induction heating process. The impact response of was characterized by two modes of failure which differed by failure or nonfailure in tension of the bottom titanium ply. The ductility of titanium caused buckling by yielding whereas the brittle adjacent composite ply lead to fracture. The maximum failure force of the material correlated well with the previously reported static flexural data, and the material outperformed the commonly used graphite/epoxy.
Skip Nav Destination
e-mail: ramulum@u.washington.edu
Article navigation
April 2007
Technical Papers
Low-Velocity Impact Response Characterization of a Hybrid Titanium Composite Laminate
S. Bernhardt,
S. Bernhardt
Department of Mechanical Engineering,
University of Washington
, Seattle, WA 98195
Search for other works by this author on:
M. Ramulu,
M. Ramulu
Department of Mechanical Engineering,
e-mail: ramulum@u.washington.edu
University of Washington
, Seattle, WA 98195
Search for other works by this author on:
A. S. Kobayashi
A. S. Kobayashi
Department of Mechanical Engineering,
University of Washington
, Seattle, WA 98195
Search for other works by this author on:
S. Bernhardt
Department of Mechanical Engineering,
University of Washington
, Seattle, WA 98195
M. Ramulu
Department of Mechanical Engineering,
University of Washington
, Seattle, WA 98195e-mail: ramulum@u.washington.edu
A. S. Kobayashi
Department of Mechanical Engineering,
University of Washington
, Seattle, WA 98195J. Eng. Mater. Technol. Apr 2007, 129(2): 220-226 (7 pages)
Published Online: July 13, 2006
Article history
Received:
November 28, 2005
Revised:
July 13, 2006
Citation
Bernhardt, S., Ramulu, M., and Kobayashi, A. S. (July 13, 2006). "Low-Velocity Impact Response Characterization of a Hybrid Titanium Composite Laminate." ASME. J. Eng. Mater. Technol. April 2007; 129(2): 220–226. https://doi.org/10.1115/1.2400272
Download citation file:
Get Email Alerts
Modeling Growth and Viscous Flow of Oxide on Cylindrical Silicon Surfaces Including Piezoviscous Inhibition
J. Eng. Mater. Technol (April 2025)
Thermal Conductivity of 3D-Printed Metal Using Extrusion-Based Metal Additive Manufacturing Process
J. Eng. Mater. Technol (April 2025)
Related Articles
Scaling of Strength of Metal-Composite Joints—Part I: Experimental Investigation
J. Appl. Mech (January,2010)
Response of Resin Transfer Molded (RTM) Composites Under Reversed Cyclic Loading
J. Eng. Mater. Technol (January,1996)
A Constitutive Model for Distributed Microcracking In Titanium Matrix Composite Laminae
J. Eng. Mater. Technol (October,2000)
Characterization of Fatigue Behavior in Cross-Ply Laminate of SCS-6/Ti-15-3 Metal Matrix Composite at Elevated Temperature
J. Eng. Mater. Technol (October,1992)
Related Proceedings Papers
Related Chapters
In Situ Observations of the Failure Mechanisms of Hydrided Zircaloy-4
Zirconium in the Nuclear Industry: 20th International Symposium
Constant Strain Rate Technique for Assessing Stress-Corrosion Susceptibility
Stress Corrosion—New Approaches
Two-Dimensional Delamination Growth in Composite Laminates Under Compression Loading
Composite Materials: Testing and Design (Eighth Conference)